POLYAMIDE 12 HOSES DIN 73378 / 74324 HIPHL / PHL / PHLY / HL

FLEXAMIDE PA12 HIPHL tubes are constructed from highperformance polyamide 12 (PA12), a durable plastic material derived from oil. This robust material ensures FLEXAMIDE PA12 HIPHL tubes meet the strict requirements of DIN 73378 and DIN 74324 standards. Flexamide tubes offer outstanding mechanical and chemical resistance within the temperature range of -40°C to +130°C.

Product code External Internal Thickness Tolerances Bending Radius Roll Length Working pressure at 23°C Burst pressure at 23°C Available Colours
                  BL TR BU YL RD GR
PA121530 3 mm 1,5 mm 0,75 mm +- 0,1 mm 15 mm 200 m 49 bar 147 bar        
PA122040 4 mm 2 mm 0,75 mm +- 0,1 mm 20 mm 200 m 49 bar 147 bar      
PA122540 3 mm 2,5 mm 0,75 mm +- 0,1 mm 20 mm 200 m 34 bar 102 bar
PA123050 5 mm 3 mm 1 mm +- 0,1 mm 30 mm 200 m 37 bar 111 bar        
PA123350 5 mm 3,3 mm 0,85 mm +- 0,1 mm 30 mm 100 m 31 bar 93 bar          
PA123060 6 mm 3 mm 1,5 mm +- 0,1 mm 25 mm 100 m 49 bar 147 bar        
PA124060 6 mm 4 mm 1 mm +- 0,1 mm 35 mm 200 m 29 bar 87 bar
PA124480 8 mm 4,4 mm 1,8 mm +- 0,1 mm 45 mm 100 m 38 bar 114 bar          
PA125580 8 mm 5,5 mm 1,25 mm +- 0,1 mm 35 mm 100 m 27 bar 81 bar          
PA125580 8 mm 5,5 mm 1,25 mm +- 0,1 mm 35 mm 100 m 27 bar 81 bar          
PA126080 8 mm 6 mm 1 mm +- 0,1 mm 40 mm 100 m 21 bar 63 bar
PA126090 9 mm 6 mm 1,5 mm +- 0,15 mm 45 mm 100 m 29 bar 87 bar          
PA126095 9,5 mm 6 mm 1,75 mm +- 0,15 mm 45 mm 100 m 30 bar 90 bar          
PA127095 9,5 mm 7 mm 1,25 mm +- 0,15 mm 50 mm 100 m 20 bar 60 bar          
PA127010 10 mm 7 mm 1,5 mm +- 0,15 mm 60 mm 100 m 24 bar 72 bar          
PA127510 10 mm 7,5 mm 1,25 mm +- 0,15 mm 60 mm 100 m 21 bar 63 bar          
PA128010 10 mm 8 mm 1 mm +- 0,15 mm 60 mm 100 m 16 bar 48 bar      
PA128011 11 mm 8 mm 1,5 mm +- 0,15 mm 60 mm 100 m 23 bar 69 bar          
PA128012 12 mm 8 mm 2 mm +- 0,15 mm 60 mm 100 m 29 bar 87 bar          
PA129012 12 mm 9 mm 1,5 mm +- 0,15 mm 60 mm 100 m 21 bar 63 bar
PA121012 12 mm 10 mm 1 mm +- 0,15 mm 85 mm 100 m 12 bar 36 bar        
PA1210125 12,5 mm 10 mm 1,25 mm +- 0,15 mm 80 mm 100 m 16 bar 48 bar          
PA1290127 12,7 mm 9 mm 1,85 mm +- 0,15 mm 60 mm 50 m 22 bar 66 bar          
PA121014 14 mm 10 mm 2 mm +- 0,15 mm 75 mm 50 m 24 bar 72 bar          
PA121114 14 mm 11 mm 1,5 mm +- 0,15 mm 85 mm 50 m 16 bar 48 bar          
PA121214 14 mm 12 mm 1 mm +- 0,15 mm 95 mm 50 m 11 bar 33 bar          
PA121215 15 mm 12 mm 1,5 mm +- 0,15 mm 90 mm 50 m 16 bar 48 bar          
PA1212515 15 mm 12,5 mm 1,25 mm +- 0,15 mm 95 mm 50 m 13 bar 39 bar          
PA121216 16 mm 12 mm 2 mm +- 0,15 mm 95 mm 50 m 21 bar 63 bar          
PA121418 18 mm 14 mm 2 mm +- 0,15 mm 100 mm 50 m 18 bar 54 bar          
PA121620 20 mm 16 mm 2 mm +- 0,15 mm 180 mm 50 m 16 bar 48 bar          
PA121822 22 mm 18 mm 2 mm +- 0,15 mm 180 mm 50 m 14 bar 42 bar          

This table is valid for PA 12 HIPHL types. For all types please check page 45-46.

Pressure values in the table are estimated and may vary depending on ambient and operating conditions. Product performance may vary
depending on the application conditions implemented by users. (Tested per DIN 73378/74324)

Tolerance

Tolerance on external diameter as per DIN 73378 / 74324

Raw Material Properties
  PHLY PHL HIPHL
Shore Hardness 67 D 65 D 63 D
Density 1,02 g/cm3 1,02 g/cm3 1,02 g/cm3
Melting Point 178 C 175 C 173 C
Water Absorption %1,4 %1,4 %1,4
Humidity Absorption %0,7 %0,7 %0,7
Tensile Modulus 550 Mpa 450 Mpa 400 Mpa
PHLY PHL HIPHL PRESSURE COMPARISON BAR 23°C
Size PHLY PHL HIPHL
6x8 mm 26 19 21D
 
TEMPERATURE RANGE

-40°C / +130°C

CHEMICAL RESISTANCE
Check the table.
PRESSURE VARIATION

Performance percentage according to temperature.

% Press Temp
100% 23° C
87% 30° C
74% 40° C
64% 50° C
57% 60° C
52% 70° C
47% 80° C
44% 90° C
40% 100° C
36% 110° C
33% 120° C
30% 130° C
 

HI: PA12 impact modified
P: Plasticized
H: Heat stabilized against thermal aging 
IL: Light stabilized for better UV resistance
Y: PA12 modified for higher working pressures

Properties
  • High impact and notched impact strength, even in cold
  • environments
  • Excellent resistance to cracking and breaking
  • Maintains good pressure resistance at elevated temperatures
  • Durable against abrasion
  • Dimensionally stable
  • Resistant to a wide range of chemicals, including oils, greases,
  • fuels, oxidizing agents, hydraulic fluids, and salt solutions
  • Low density
Applications
  • Automotive fluid and air lines
  • Central lubrication systems
  • Compressed air systems
  • Measurement and control technology
  • Road vehicle air brake tubing
  • Fuel lines
Packing

Standart olarak plastik makaralı, müşteri isteğine bağlı paketleme özelleştirilebilir.

Download Product Catalog

Would You Like to Participate in Our Survey?

Your Opinions Are Important to Us.
Send Message